For the interior coating of ductile cast iron pipes for water supply! Fast-curing epoxy resin-based powder coating.

Rapid curing with high-temperature preheating! Developed for the internal coating of ductile iron pipes, irregular pipes, and valves for water supply, it excels in rapid curing, corrosion resistance, and water quality suitability!

The powder coating "Toa Powder #6150 / #6150F" is a fast-curing, corrosion-resistant, and water quality-appropriate powder coating developed for the interior coating of ductile iron pipes and fittings for water supply, as well as for valve interiors. It protects the inner surfaces of cast iron pipes used in the important social infrastructure of water supply and sewage systems. It is an environmentally friendly coating that does not contain organic solvents. The substrate is preheated in a drying oven to a high temperature, coated outside the oven, and cured using that preheating. Automation of the coating process is possible, allowing for labor-saving solutions! 【Features】 - Preheating coating (dry film thickness of 300 to 1,200 μm) is possible, and it cures quickly. - It conforms to "JWWA G 112" for epoxy resin powder coatings for the interior of ductile iron pipes for water supply. - It has excellent coating workability. 【Applications】 - Ductile iron straight pipes for water supply and sewage - Fittings and valve interiors

basic information

【Baking Conditions (Workpiece Temperature)】 Start Temperature for Coating: 210–240℃ End Temperature for Coating: Above 190℃ *If the end temperature for coating falls below 190℃, please perform post-heating at 180℃–210℃ for 10 minutes. 【Paint Properties】 Average Particle Size: 34–55μm Dry Film Thickness: 300–1,200μm Standard Coating Amount: 450/m², calculated without loss at 300μm. However, this may vary depending on the hue. *For more details, please contact us or refer to the PDF.